Quality Assured Used in High Temperature Huayue Heat Resistant Conveyor Belting System Cc Nn Ep St

• Customization: Available
• Type: Conveyor Belt
• Feature: Wear-resistant, Heat-resistant, Tear-resistant, Flame-resistant, Cold-resistant
• Performance: Heat Resistant
• Standards: DIN, Rma, as, Jisk, SABS,BS, ISO
• Certificate: ISO,BV,SGS,Sans
• Width: 100-2200mm
• Thickness: 5-30
• Types: 0-800c Heat Resistant
• Material Handle: Industry, Agriculture, Cement, Quarry
• Tensile Strength (MPa): 5-12MPa
• Color: Black
• Transport Package: PVC Water Proof Cloth
• Specification: DIN; AS; RMA; SABS; BS; JISK
• Trademark: Huayue
• Origin: Baoding City Hebei Province China
• HS Code: 4010120000
• Production Capacity: 5000 Meter Per Day

Product Description

Rubber Heat Retardant Conveyor Belt for Mining Industry

Characteristics (Rubber Cover Anti High Temperature)
The belt carcass of this product is EP fabric of high modulus, low shrink, and high breaking tensile strength.Cover rubber of this product uses EPDM rubber or Chloro-butyl rubber that has very good high temperature resistance.The belt is made with extra care after mixing rubber with high temperature resistant materials, assembling and vulcanizing.

Top 5 conveyor belt manufacture in china
Huayue Heat Resistant Conveyor Belt Competitive Advantage
1.Plies:1-10ply
2:Width:400-2200mm
3.Thickness:4-30mm
4.Working Temperature:0 - 800ºC
5.Abrasion resistant & High Tensile Strength
6.ISO9001:2008, SGS, Bureau Veritas Certificate.
7.More Than 30 years professional experience.(Since 1982)
8.International Standard:DIN, BS, AS, RMA, AS, JISK, SABS etc

Abour us
Huayue brand is the Top 5 manufacturers and exporters of Conveyor Belt in China.Our range of conveyor belts are highly appreciated by our clients due to its heat resistance feature and other availability in various sizes and designs.These are dimensionally accurate as per international standards.

Our best quality based on:
Manufacturer
Experience in Cooperate with Fortune 500 Companies
Professional Engineering Capability
Stable Quality
Reasonable Price
Small Orders Accepted
Continuous Improvements
High Product Performance
Prompt Delivery
Professional Service
 

Item	Detail	Class
		T1	T2	T3	T4
		Test temperature
		≤100°C	≤125°C	≤150°C	≤175°C
		Change range allowed
Hardness	Difference before and after aging(IRHD)	20	20	±20	±20
	Maximum value after aging(IRHD)	85	85	85	85
Tensile Strength	Change rate after aging/%	-25	-30	-40	-40
	Minimum value after aging/MPa	12	10	5	5
Breaking Elongation	Change rate after aging/%	-50	-50	-55	-55
	Minimum value after aging/%	200	200	180	180
Standard Of Conveyor belt:DIN, BS, AS, RMA, AS, JISK, SABS etc

Physical and mechanical properties of the heat resistant covering layer after tested should be in accordance with the following table:

Project		The type
		T1	T2	T3	T4
		Change the range
Hardness	Draw the intensity	+20	+20	+20	+20
	Maximum after wearing out	85
Draw the intensity	The minimum value Mpa after wearing out	12	10	5	5
	Performance rate of change /%	-25	-30	-40	-40
Break person who extend	Performance rate of change /%	-50	-50	-55	-55
	After aging rate of change /%	200	200	180	180

Physical property of the cover rubber after heat test shall conform to the values specified in the table.

Item		Type
		Type I		Type II			Type III
		Variable range
Hardness	Difference before and after ageing (IRHD)				±20
	Max.Value after ageing (IRHD)	85
Tensile strength	Variable rate in performance   <=	25	30			40
	Min.Value after ageing Mpa	12	10			5
Rate of elongation at break	Variable rate in performance% <=	50				55
	Min.Value after ageing	200				180

Abrasive wear of the cover rubber

Type   Item level	Abrasive wear
	Type I	Type II	Type III
First quality	0.8	1.0	1.0
Accepts	1.0	1.2	1.2

Layer adhesion strength

Item	Interlayer of cloth	Cover layer and cloth interlayer
		Thickness of the cover layer≤1.5mm	Thickness of the cover layer>1.5mm
The average value of the longitudinal specimen shall be no less than	3.0	2.2	2.6
The peak value of the longitudinal specimen	2.0	1.6	2.0